Oyar, PerihanDurkan, RukiyeProtetik Diş Tedavisi / Prosthetic Dental Treatment2024-05-252024-05-25202300013-55851862-278X10.1515/bmt-2022-03382-s2.0-85150514730https://doi.org/10.1515/bmt-2022-0338https://hdl.handle.net/20.500.14517/1276The strength of zirconia ceramic materials used in restorations is dependent upon sintering. Varying sintering protocols may affect the biaxial flexural strength of zirconia materials. This in vitro study was conducted to investigate the effects of sintering parameters on the biaxial flexural strength of monolithic zirconia. Two different monoblock zirconia ceramics were used. Following coloration, samples of both types of ceramics were divided into groups according to whether or not biaxial flexural strength testing was performed directly after sintering or following thermocycling. Biaxial flexural strength data was analysed with a Shapiro Wilk normality test, followed by 1-way ANOVA, Tukey post hoc tests for inter-group comparisons, and paired samples t-tests for intra-group comparisons. A significant difference was found between the biaxial flexural strengths of Zircon X and Upcera ceramics before thermocycling (p < 0.05). In both Zircon X and Upcera ceramic groups, the thermocycling process created a significant difference in the biaxial flexural strength values of the ceramic samples in Group 6 (p < 0.05) which had the slowest heating rate and longest holding time. The zirconia ceramics have higher BFS at higher heating rates either before or after thermocycling. The holding time has significant effects on thermocycling and flexural strength. The zirconia achieved its optimum strength when it sintered at longer time regardless of heating rates.eninfo:eu-repo/semantics/closedAccessdental ceramicflexural strengthmonolithic zirconiasinteringArticleQ4Q3684437443WOS:00095312390000136930871